inorganic filler

Chemical constitution and microscopic pattern of the inorganic filler in a corona resistant magnetic wire insulating coating was tested and analyzed.

测试和分析了某型耐电晕电磁线绝缘漆中无机填料的化学组成和微观形貌，并测试该电磁线绝缘漆的紫外可见光吸收谱。

Dental filling materials contain resin of polymer, inorganic filler and photoinitiator system, which are used in dental restoration.

齿科充填复合材料是由高分子基质、无机填料及光引发剂体系组成的复合物，主要用于齿科的修复。

Routes of reaction type inorganic filler have been explored in experiments, and an encouraging result has been achieved.

试验探索了反应型无机填料的路线，已取得了可喜的成果。

Titanyl sulfate also can be prepared titania-coated inorganic filler composite particles, raise the ratio between performance and price of powder material.

用硫酸氧钛还可以制备二氧化钛包覆无机物填料的复合粒子，提高粉体材料的性价比。

Using the test means of FTIR, SEM, XRD and DSC-TGA to characterize the effect of surface modification of inorganic filler filler 、 the microstructure and composition of fireproof coating, and discussed the fireproofing mechanism.

采用傅立叶红外光谱、扫描电镜、X射线衍射、热重分析等测试手段，对无机填料表面改性效果、防火涂料的微观结构及成分进行了表征，并对防火涂料的防火机理进行了探讨。

Jumbo Tile is a thick-layer weather-shield coating adopting inorganic filler, pigments, and high-end water-based resin.

强保是一种采用高级水性耐候树脂，配合天然无机填料、颜料调制而成的耐候性厚涂材涂料。

Studied the influence of the expanded graphite and magnesium hydroxide as flame retardant additives on fire properties of coating 、 the titanium dioxide and talc as inorganic filler on the coating properties, and confirmed the optimum process conditions.

研究了无机阻燃剂膨胀石墨和Mg（OH）2对涂料耐火性能的影响，研究了填料TiO2和滑石粉对防火涂料性能的影响，确定了最佳工艺条件。

A friction resistant materials for the vehicle was developed, which was modified by BMI with cashew shell oil and phenolic resin blend as the matrix and the carbon fiber, steel fiber and inorganic filler as reinforced materials.

本文研制了以BMI，腰果壳油，酚醛树脂三元体系共混改性的树脂为基体，碳纤维，金属丝以及无机填料为增强材料的车用摩擦材料。

The resin matrix and inorganic filler were studied in this paper.

以气相SiO2作为无机填料，从树脂基质和填料两个方面研究了可见光固化齿科用复合树脂的挠曲强度。

A matrix material with radiation resistance well processability was made by a simple processing technology of selecting matrix resin, inorganic filler adding well property radiation resistant additives.

通过对母料载体树脂的筛选，无机填料的选择，添加性能优良的耐辐射助剂，制成了具有耐辐射性能、加工性能良好的母料，该母料的制备工艺简单。

In this paper, silane coupling agent KH-570 was used to treat talc and hollow glass microsphere, the mechanical properties of cast UP resin and its GFRP filled with modified inorganic filler were also tested.

本文用硅烷偶联剂KH－570对滑石粉、空心玻璃微珠进行表面处理，并对改性无机填料填充UP树脂浇铸体及其GFRP的力学性能进行了测试。